 產(chǎn)品詳細(xì)介紹 |
|
項(xiàng) 目 \ 牌 號 |
高熱震耐火制品 |
紅柱石制品 |
|
RDL-75 |
ML-72 |
SDHA55 |
HRN-48 |
HRN-42 |
HLE |
SDHB |
SDHD |
SDHS |
SDDE |
SDHR |
| Al2O3 % |
≥75 |
≥72 |
≥55 |
≥48 |
≥42 |
≥57 |
≥65 |
≥53 |
≥57 |
≥55 |
≥60 |
Fe2O3 %
|
≤1.2 |
≤1.2 |
≤0.8 |
≤1.5 |
≤1.5 |
≤1.2 |
≤0.8 |
≤1.0 |
≤1.0 |
|
≤0.8 |
TiO2 %
|
|
|
|
|
|
|
≤0.5 |
≤0.6 |
≤0.5 |
|
≤0.5 |
| K2O+Na2O % |
≤0.5 |
|
|
|
|
≤0.6 |
≤0.6 |
≤1.2 |
≤0.6 |
≤1.2 |
≤0.6 |
≤1.2 |
≤1.0 |
≤0.6 |
≤1.2 |
雜質(zhì) %
|
|
|
|
|
|
|
≤0.7 |
≤0.7 |
≤0.7 |
|
≤0.7 |
|
耐火度 ℃ |
≥1790 |
≥1790 |
≥1760 |
≥1750 |
≥1750 |
|
|
|
|
|
|
顯氣孔率 %
|
≤22
|
≤23
|
≤20
|
≤21(24)
|
≤23(24)
|
≤20(22)
|
≤20 |
≤20 |
≤20 |
≤24 |
≤20 |
常溫耐壓強(qiáng)度 Mpa
|
≥60 |
≥50 |
≥55 |
≥40 |
≥40 |
≥40(30)
|
≥50 |
≥40
|
≥40 |
≥40 |
≥40 |
常溫抗折強(qiáng)度 Mpa
|
|
|
|
|
|
≥15(12) |
≥18 |
≥15 |
|
|
|
| 荷重軟化溫 ℃ |
T2≥1550 |
KD≥1550 |
KD≥1550 |
T2≥1550 |
T2≥1520 |
T0.5≥1420
T2≥1580 |
T0.5≥1520
T2≥1630 |
T0.5≥1350
T2≥1490 |
T0.5≥1470
T2≥1580 |
T2≥1580 |
T0.5≥1460
T2≥1600 |
0.2MPa蠕變率
(20～50)h %
|
1550℃×50h
≤0.8 |
|
|
|
|
|
1500 ℃
≤0.2 |
1350 ℃
≤0.2 |
1400 ℃
≤0.2 |
1450 ℃
≤0.2 |
1450 ℃
≤0.2 |
重?zé)�變化率 %
|
1550 ℃×2h
+0.1～-0.2 |
1450 ℃×2h
±0.1 |
1450 ℃×2h
±0.1 |
1450 ℃×2h
0～-0.2 |
1450 ℃×2h
0～-0.2 |
1500 ℃×4h
±0.2 |
1500 ℃×4h
±0.2 |
1400 ℃×4h
±0.2 |
1500 ℃×4h
±0.2 |
1500 ℃×4h
±0.2 |
1500 ℃×4h
±0.2 |
熱震穩(wěn)定性,次(1100℃ 水冷)
|
≥15 |
≥100 |
≥30 |
≥30 |
≥30 |
≥20 |
|
950℃
≥30 |
950℃
≥30 |
|
|
| 使用部位 |
拱頂 |
燃燒室 |
蓄熱室、拱頂、
大墻、格子 |
熱風(fēng)管道 |
|
|
|
|
| |
注：括號中的數(shù)值適用于手工成型制品 | |
|